ASTM A691 5CR Class30 Tube

$833≥1Ton

Jenis pembayaran:	L/C,T/T,Paypal
Inkoterm:	FOB,CFR,CIF,EXW,Express Delivery,DDP,DDU
Min. Memesan:	1 Ton
Transportasi:	Ocean,Land,Air,Express
Pelabuhan:	TIANJIN,LIANYUNGANG,QINGDAO

Hubungi sekarang

Deskripsi Produk

Atribut Produk

& pengiriman paket

Deskripsi Produk

Atribut Produk

Model No: ASTM A691 5CR CLASS30 TUBE

Merek: Gnee

Standar: ASTM, bs, GB, JIS, KERIUHAN, API

Bahan: 10MoWVNb, ST35-ST52, 15NiCuMoNb5, STPA22-STPA26, Paduan Cr-Mo, 10 # -45 #, MO, API J55-API P110, Paduan CrNi, 10Cr9Mo1VNb, A53-A369, STBA20-STBA26, STPG42, Paduan Mn-V, Q195-Q345, 16mn, STB35-STB42

Bentuk Bagian: Bulat

Tempat Asal: Cina

Aplikasi: Pipa Fluida, Pipa Boiler

Sertifikasi: ce, UL, Bsi, API

Pengobatan Permukaan: Dilapisi tembaga, Galvanis

Tabung Khusus: Pipa Dinding Tebal

Apakah Paduan: Apakah Paduan

Toleransi: ± 1%

Kategori: Pipa Baja Dilas, Pipa Dilas Spiral, Tabung Persegi

Layanan Pengolahan: Pengelasan, Pemotongan, Dekorasi, Meninju, Pembengkokan

& pengiriman paket

Menjual unit	:	Ton
Tipe paket	:	BUNDEL
Unduh	:

The file is encrypted. Please fill in the following information to continue accessing it

Deskripsi Produk

ASTM A691 Pipa Baja Karbon dan Paduan, Disasing Fusi Listrik untuk Layanan Tekanan Tinggi pada Suhu Tinggi

TABLE 1 Plate Materials
Pipe Grade	Type of Steel	ASTM Specification		HB, max A
Pipe Grade	Type of Steel	Number	Grade	HB, max A
CM-65	carbon-molybdenum steel	A204/A204M	A	201
CM-70	carbon-molybdenum steel	A204/A204M	B	201
CM-75	carbon-molybdenum steel	A204/A204M	C	201
CMSH-70	carbon-manganese-silicon steel, normalized	A537/A537M	1
CMS-75	carbon-manganese-silicon steel	A299/A299M	. . .	. . .
CMSH-80	carbon-manganese-silicon steel, quenched and tempered	A537/A537M	2
1 ⁄ 2 CR	1 ⁄ 2 % chromium, 1 ⁄ 2 % molybdenum steel	A387/A387M	2	201
1CR	1 % chromium,1 ⁄ 2 % molybdenum steel	A387/A387M	12	201
1 1 ⁄ 4 CR	1 1 ⁄ 4 % chromium,1 ⁄ 2 % molybdenum steel	A387/A387M	11	201
2 1 ⁄ 4 CR	2 1 ⁄ 4 % chromium, 1 % molybdenum steel	A387/A387M	22	201
3CR	3 % chromium, 1 % molybdenum steel	A387/A387M	21	201
5CR	5 % chromium,1 ⁄ 2 % molybdenum steel	A387/A387M	5	225
9CR	9 % chromium, 1 % molybdenum steel	A387/A387M	9	241
91	9 % chromium, 1 % molybdenum, vanadium, niobium C	A387/A387M	91 B	241

TABLE 2 Heat Treatment Parameters A
Pipe Grade	ASTM Specification	Post-Weld Heat-Treat Temperature Range (StressRelieving), °F (°C)	Normalizing Temperature, max unless otherwise noted, °F (°C)	Quenching Temperature, max unless otherwise noted，°F (°C)	Tempering Temperature, min, °F(°C)
CM-65	A204/A204M	1100 to 1200 [590 to 650]	1700 [925]	. . .	. . .
CM-70	A204/A204M	1100 to 1200 [590 to 650]	1700 [925]	. . .	. . .
CM-75	A204/A204M	1100 to 1200 [590 to 650]	1700 [925]	. . .	. . .
CMSH-70	A537/A537M	1100 to 1200 [590 to 650]	1700 [925]	. . .	. . .
CMS-75	A299/A299M	1100 to 1200 [590 to 650]	1700 [925]	. . .	. . .
CMSH-80	A537/A537M	1100 to 1200 [590 to 650]	B	1700 [925]	1100 to 1250 [590 to 675]
1 ⁄ 2 CR	A387/A387M	1100 to 1300 [590 to 705]	1850 [1010]	1700 [925]	1150 to 1375 [620 to 745]
1CR	A387/A387M	1100 to 1350 [590 to 730]	1850 [1010]	1700 [925]	1150 to 1375 [620 to 745]
11 ⁄ 4 CR	A387/A387M	1100 to 1375 [590 to 745]	1850 [1010]	1700 [925]	1150 to 1375 [620 to 745]
21 ⁄ 4 CR	A387/A387M	1200 to 1400 [650 to 760]	1850 [1010]	1700 [925]	1250 to 1400 [675 to 760]
3CR	A387/A387M	1200 to 1400 [650 to 760]	1850 [1010]	1700 [925]	1250 to 1400 [675 to 760]
5CR	A387/A387M	1200 to 1400 [650 to 760]	1850 [1010]	1650 [900]	1300 to 1400 [705 to 760]
9CR	A387/A387M	1325 to 1375 [715 to 745]	C	. . .	1325 to 1375 [715 to 745]
91	A387/A387M	1350 to 1420 [730 to 770]	1900 to 2000[1040 to 1095]	1900 min[1040 min]	1350 to 1440 [730 to 780]

Class designations are as follows
Class	Heat Treatment on Pipe	Radiography, see Section	Pressure Test, see Section
10	none	none	none
11	none	9	none
12	none	9	8.3
13	none	none	8.3
20	stress relieved, see 5.3.1	none	none
21	stress relieved, see 5.3.1	9	none
22	stress relieved, see 5.3.1	9	8.3
23	stress relieved, see 5.3.1	none	8.3
30	normalized, see 5.3.2	none	none
31	normalized, see 5.3.2	9	none
32	normalized, see 5.3.2	9	8.3
33	normalized, see 5.3.2	none	8.3
40	normalized and tempered, see 5.3.3	none	none
41	normalized and tempered, see 5.3.3	9	none
42	normalized and tempered, see 5.3.3	9	8.3
43	normalized and tempered, see 5.3.3	none	8.3
50	quenched and tempered, see 5.3.4	none	none
51	quenched and tempered, see 5.3.4	9	none
52	quenched and tempered, see 5.3.4	9	8.3
53	quenched and tempered, see 5.3.4	none	8.3